1.75mm

Bambu Lab PA6-CF

Product SKU: N05-K0-1.75-1000-spl

$86.69 $101.99

Available Stock:
Loading...

Benefits of Buying Bambu Lab from Shop3D.ca

Certified & Approved Products

ESA-approved and TÜV-certified printers for the Canadian market
Approved vendor for government, education, and diversity-certified supplier

Comprehensive Training & Support

Free onboarding training for educational institutions
Account managers providing recommendations and best practices

Warranty & Repair Services

Bambu Lab warranty with local troubleshooting and parts
Local repair facility and warranty facilitation

Convenient & Responsive Local Support

Immediate response via phone or chat
Local pickup available in Vancouver and Mississauga

Overview

Bambu PA6-CF is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly high stiffness and strength properties in dry environments and maintains exceptional heat resistance and impact resistance. Similar to other Bambu CF Filaments, these outstanding mechanical properties make it an ideal choice for printing fixtures, clamps, automotive and mechanical components and various structural and engineering parts that used in dry environments.

Product Features

Superior Strength and Stiffness
Toughness & Vibration Resistance
Exceptional Thermal Resistance
Comes with High Temperature Reusable Spool
Diameter: 1.75mm +/- 0.03mm

Printing Tips

• Bambu PA6-CF needs proper drying before printing: recommended drying temperature is 80 ℃ for 10 hours in a blast drying oven, or 90 ℃ for 12 hours on heat bed. (Do not exceed 100 ℃ because the spool may melt). For more details, please refer to: Printing tips for Engineering materials on WIKI.
• Bambu PA6-CF will experience a decrease in strength and stiffness after absorbing water,making it not recommended for printing models with high requirements for strength, stiffness, and dimensional stability, especially thin and elongated models. The prints of PA6-CF usually become tougher and more resistant to impacts, drops, and collisions when they get damp, you can dampen and soften the prints in advance if the model requires high toughness.
• When printing a model with support, it is necessary to remove the support structure within 2 hours to prevent it from being difficult to remove after being damp and softened. Please dry the prints and let them cool down if it is difficult to remove the support, and then remove the support in time.
• Fully impregnating the surface of the prints with paint, wax and other water-proof coatings can inhibit water absorption and prevent them from becoming soft.

Recommended Print Settings

Drying Settings before Printing: 80 °C, 8 - 12 h
Printing and Keeping Container's Humidity: < 20% RH (Sealed, with Desiccant)
Nozzle Temperature: 260 - 290 °C
Bed Temperature (with Glue): 80 - 100 °C
Printing Speed: < 100 mm/s

Physical Properties

Density: 1.09 g/cm³
Vicar Softening Temperature: 212 °C
Heat Deflection Temperature: 186 °C
Melting Temperature: 223 °C
Melt Index: 6.8 ± 0.6 g/10 min

Mechanical Properties

Tensile Strength: 102 ± 7 MPa
Breaking Elongation Rate: 5.8 ± 1.6 %
Bending Modulus: 5460 ± 280 MPa
Bending Strength: 151 ± 8 MPa
Impact Strength: 40.3 ± 2.5 kJ/m²

Accessory Compatibility

	Recommended	Not Recommended
Build Plate	Engineering Plate, High Temperature Plate or Textured PEI Plate	Cool Plate
Hotend	Hardened Steel 0.4 / 0.6 (recommended) / 0.8 mm	Hotend with Stainless Steel Nozzle (all size) Hotend with Hardened Steel Nozzle (0.2 mm)
Glue	Glue Stick Bambu Liquid Glue	/

Highlights

* The prints of PA6-CF will be tougher after putting in humid environment more than 1 day.

Superior Strength and Stiffness

As a new member of Bambu high performance filaments, PA6-CF keeps superior stiffness and strength properties in dry environments, it is perfect for printing load-bearing structural components.

Impact & Vibration Resistance

Bambu PA6-CF offers excellent impact resistance, ensuring effective vibration resistance for your prints. It is commonly used to print models that need to withstand impact, collision, and vibration.

	Normal PA-CF	PA6-CF	Improved %
Strength (Bending Strength - XY, dry state)	128 MPa	151 MPa	18%
Stiffness (Bending Modulus - XY, dry state)	4420 MPa	5460 MPa	24%

Exceptional Thermal Resistance

Filament	PLA Basic	PETG Basic	ABS	ASA	PC	PA6-CF	PAHT-CF	PET-CF
Heat Deflection Temperature / °C (0.45 MPa)	57 °C	69 °C	87 °C	100 °C	117 °C	186 °C	194 °C	205 °C

Parameters Comparison

	Normal PA6-CF	PA6-CF	PAHT-CF
Composition	Nylon 6, carbon fiber	Nylon 6, carbon fiber	PA12 and other long-chain PA, carbon fiber
AMS Compatibility	NO	NO	YES
Dry Out Before Use	Required	Required	Required
Printing Speed	< 100 mm/s	< 100 mm/s	< 100 mm/s
Printer Type	Enclosure	Enclosure	Enclosure
Toughness (Impact Strength - XY, dry state)	35.7 kJ/m²	40.3 kJ/m²	57.5 kJ/m²
Toughness (Impact Strength - XY, wet state)	65.4 kJ/m²	57.2 kJ/m²	62.3 kJ/m²
Strength (Bending Strength - XY, dry state)	141 MPa	151 MPa	125 MPa
Strength (Bending Strength - XY, wet state)	67 MPa	95 MPa	115 MPa
Layer Strength (Bending Strength - Z, dry state)	72 MPa	80 MPa	61 MPa
Layer Strength (Bending Strength - Z, wet state)	31 MPa	45 MPa	49 MPa
Stiffness (Bending Modulus - XY, dry state)	4870 MPa	5460 MPa	4230 MPa
Stiffness (Bending Modulus - XY, wet state)	1890 MPa	3560 MPa	3640 MPa
Layer Adhesion (Impact Strength - Z, dry state)	11.6 kJ/m²	15.5 kJ/m²	13.3 kJ/m²
Heat Resistant (HDT, 0.45 MPa)	177 °C	186 °C	194 °C
Saturated Water Absorption Rate / % (25 °C，55% RH)	3.80	2.35	0.88

Downloads