Raise3D Industrial PET GF Filament - 1.75mm (1kg)

Raise3D Industrial PET GF Filament - 1.75mm (1kg)

Raise3D Industrial PET GF Filament - 1.75mm (1kg)

Glass fiber reinforced PET filament with high strength, stiffness, and dimensional stability.
Color
SKU: [S]5.11.19034A01
$100.00 CAD
Sale
Sold out

Price

$100.00 CAD

Stock

Request a Quote | Email This Page

Filament Details

Performance ratings are intended as a general comparison guide. Refer to the Technical Data Sheet (TDS) for detailed specifications and certified values.
Raise3D Industrial PET GF 1.75mm Filament (1KG) is an engineering-grade PET filament reinforced with glass fibers to deliver enhanced strength, stiffness, heat resistance, and dimensional stability. Designed for demanding industrial applications, it provides excellent mechanical performance, low shrinkage, and improved resistance to wear and deformation compared to standard PET. Ideal for functional parts, tooling, and components requiring long-term reliability.
Applications
  • Automobile
  • End-use parts
  • Jigs & Fixtures
  • Manufacture tools
  • Electrical and electronics (E&E) industry

Documentation

Resistant to Temperature Cycling.

See TDS for Details

Intermediate Material

See TDS for information

Enclosed Chamber Recommended

Helps prevent warping and layer separation

Abrasive Material

A hardened nozzle is Required

Technical Specs

Overview
Net Weight 1kg
Material Compatibility
Material Diameter / Thickness 1.75mm

Product Highlights

Top Features

Raise3D Industrial PET GF is a glass fiber-reinforced composite filament based on PET (Polyethylene terephthalate). Well-dispersed glass fibers enhance the rigidity, strength, heat, and chemical resistance of PET matrix. After annealing, PET GF stabilizes its heat resistance at around 120 ℃, with tensile modulus and strength of over 4.1 GPa and 70 MPa respectively. Compared to glass fiber-reinforced Nylon filament, the high printability, dimensional stability, high creep resistance, and low moisture absorption makes PET GF an ideal choice for reliable glass fiber composite printing for strong and cost-effective end-use applications, such as jigs & fixture and functional parts. In addition, PET GF provides multiple color choices.

  • Low moisture absorption
  • High dimensional stability
  • Heat and chemical resistance
  • Creep resistance
  • Multiple colors

Benefits

  • High Strength
  • Low Moisture Absorption
  • High Performance-cost Ratio

Recommended Print Settings

  • Nozzle temperature (°C): 280-300℃
  • Bed temperature (°C): 80-100℃
  • Layer height (mm): 0.1-0.25 mm
  • Printing speed (mm/s): 35-90 mm/s
  • Cooling fan: ON
  • Drying temperature (°C): 70-80°C for 8 to 12 hours

Printing Notifications:

  • Dry PET GF at 70-80°C for 8-12 hours before printing, as low moisture content is crucial for final printed part quality.
  • After drying, we recommend storing PET GF filaments inside Raise3D Filament Dry Box during the printing process.
  • Abrasion of the brass nozzle happens frequently when printing PET GF. Using an abrasion-resistant nozzle, at minimum a Steel nozzle should be used or preferably, a SiC nozzle.
  • After printing, it is recommended to anneal the printed model in an oven at 80-100°C for 8-12 hours.
  • For a small size model (side length < 50 mm), annealing at 80℃ for 8 hours is recommended; For a medium-size model (50 mm < side length < 150 mm), annealing at 80℃ for 12 hours is recommended; For a large size model, 100°C for at least 12 hours is recommended.
  • After annealing, a maximum of 0.1 % dimensional shrinkage could be observed along the Z-axis, depending on infill and layer height, and no significant dimensional shrinkage along the XY-axes.
  • If PET GF is also used as the support material, please remove the support structure after annealing.