Bambu Lab - TPU 95A HF (1.75mm) 1kg

Product SKU: U00-W0-1.75-1000-SPL

$53.99

Available Stock:
Loading...

Color

Quantity

Not compatible with the Bambu AMS

Bambu Lab TPU 95A HF

Bambu TPU 95A HF is an optimized TPU filament designed for high-speed 3D printing. Compared to regular TPU 95A, TPU 95A HF offers an impressive 3x faster printing speed, effectively addressing the common problem of lengthy prints associated with other TPU filaments. TPU 95A HF maintains exceptional interlayer adhesion, impact resistance, flexibility, and cold-temperature resilience, just like traditional TPU filaments. Experience faster TPU printing without any compromises!

High Speed Printing

Elevate your TPU printing efficiency to the next level with Bambu TPU 95A HF, featuring a print speed that's 3 times faster than standard TPU 95A.

	Bambu TPU 95A	Bambu TPU 95A HF
Nozzle Temperature / °C	230	230
Max Volumetric Speed / (mm³/s)	3.6	12
Printing Speed / (mm/s)	44	147
Model Specimens	Diameter: 50 mm Height: 100 mm Infill:40%	Diameter: 50 mm Height: 100 mm Infill:40%

Soft and Flexible

Bambu TPU HF is an exceptionally soft and flexible filament with extraordinary impact resistance, enabling you to print parts that need to withstand impact, collision, and falling.

Accessory Compatibility

	Recommended	Not Recommended
Build Plate	Cool Plate, Engineering Plate, High Temperature Plate or Textured PEI Plate	/
Hotend	Hardened Steel Nozzle 0.4 / 0.6 / 0.8 mm) Stainless Steel Nozzle (0.4 mm)	Stainless Steel Nozzle (0.2 mm)
Glue	Bambu Liquid Glue Glue Stick	/

Recommended Printing Settings

Drying Settings (Blast Drying Oven): 70 °C，8 h
Printing and Keeping Container's Humidity: < 20% RH (Sealed，with Desiccant)
Nozzle Temperature: 220 - 240 °C
Bed Temperature (with Glue): 30 - 35 °C
Printing Speed: < 200 mm/s

Physical Properties

Density: 1.22 g/cm³
Vicat Softening Temperature: NA
Heat Deflection Temperature: NA
Melting Temperature: 183 °C
Melt Index: 36.5 ± 2.6 g/10 min

Mechanical Properties

Tensile Strength: 27.3 ± 0.8 MPa
Breaking Elongation Rate :> 650%
Bending Modulus: NA
Bending Strength: NA
Impact Strength: NA