Formlabs Surgical Guide Resin Cartridge (1 Litre OEM)

Product SKU: RS-F2-SGAM-01

Sold Out $359.00

Available Stock:
Loading...

This resin requires the use of a Formlabs Long Term LT Tank.

This resin requires Post Curing

Surgical Guide Resin for the Formlabs Form 2 / Form 3

Formlabs Surgical Guide Resin is a biocompatible material formulated for manufacturing surgical guides, pilot drill guides, and drilling templates. This application guide demonstrates each step for making 3D printed surgical guides on the Form 2 and Form 3B SLA 3D printers. Use the following workflow to ensure precise results.

SG Resin Sample

Technical Specs

Instructions for Use | Technical Data Sheet

Autoclavable, Biocompatible resin
Supports Print Resolutions: 100 and 50 microns (Form 2), 100 microns (Form 3B)
Ultimate Tensile Strength: 73 MPa
Young’s Modulus: 2.9 GPa
Elongation: 12.3%
Flexural Strength: 103 MPa
Flexural Modulus: 2.5 GPa
Hardness Shore D: 67 D

What's Included

1 Litre of Formlabs Surgical Guide Resin (OEM)

Disinfection Compatibility

Chemical Disinfection - 70% Isopropyl Alcohol for 5 minutes
Steam Sterilization: Autoclave at 134 °C for 20 minutes or Autoclave at 121 °C for 30 minutes

Overview

Surgical Guide Resin is an autoclavable, biocompatible resin for applications including 3D printing dental surgical guides for implant placement. Surgical Guide Resin was formulated specifically for Formlabs printers and rigorously tested to meet solvent disinfection and autoclave sterilization standards for implant systems.

Use Surgical Guide Resin to 3D print surgical guides, drilling templates, pilot drill guides, and device sizing templates that exceed dental demands in accuracy, part quality, and performance.

Surgical Guide Resin is a Class I Medical Device as defined in Article I of the Medical Device Directive (93/42/EEC) in the EU and in Section 201(h) of the Federal Food Drug & Cosmetic (FD&C) Act.

Notes

Material properties may vary based on part geometry, print orientation, print settings, temperature, and disinfection or sterilization methods used.

Data for post-cured samples were measured on Type IV tensile bars printed on a Form 2 printer with 100 µm Surgical Guide Resin settings, washed in a Form Wash for 20 minutes in 99 % Isopropyl Alcohol, and post-cured at 60 °C for 30 minutes in a Form Cure.