Benefits at a Glance

• High wear and abrasion resistance
• Very good low-temperature flexibility
• High tensile strength and outstanding resistance to tear propagation
• Excellent damping characteristics
• High resistance to oils, greases, oxygen and ozone
• Biocompatible

Material Properties

• Shore A Hardness: 85
• Abrasion resistance: 82mm3
• Compression set at 23°C, 72 h: 26%
• Stress at break: 34 MPa (XY), 10 MPa (ZX)
• Elongation at Break, Strain at Break: 600% (XY), 320 % (ZX)
• Tear strength: 80 kN/m (XY), 18 kN/m (XZ), 30 kN/m (ZX)

Printing Guidelines*

• Nozzle Temperature: 200-220 °C
• Build Chamber Temperature: -
• Bed Temperature: 40 °C
• Bed Material: Glass
• Nozzle Diameter: ≥ 0.4 mm
• Print Speed: 15-168 mm / s**

* The product data is provided in good faith and represents typical properties based on our current knowledge and experience; these data are not to be construed as specification limits or mini- mum values. Product properties may be changed without notice. This document does not create any liability, warranty or guarantee of product performance. It is the buyer’s responsibility to determine the suitability of Ultrafuse® products for the intended application.

** To achieve faster printing speeds, it may be necessary to raise the nozzle temperature. The highest speed mentioned has been determined through our latest tests, ensuring optimal surface quality with a 0.4mm nozzle and 0.2mm layer height. Please note that as printing technology and equipment evolve, we anticipate the possibility of achieving even faster speeds in the future.