Raise3D Industrial PET CF Filament - 1.75mm (1kg) - Black

Raise3D Industrial PET CF Filament - 1.75mm (1kg) - Black

Raise3D Industrial PET CF Filament - 1.75mm (1kg) - Black

Carbon fiber PET filament with enhanced stiffness, strength, and dimensional stability.
SKU: [S]5.11.19025A01
$115.00 CAD
Sale
Sold out

Price

$115.00 CAD

Stock

Request a Quote | Email This Page

Filament Details

Performance ratings are intended as a general comparison guide. Refer to the Technical Data Sheet (TDS) for detailed specifications and certified values.
Raise3D Industrial PET CF 1.75mm Filament (1KG) is a carbon fiber reinforced PET filament designed for high-performance engineering applications. The addition of carbon fiber improves stiffness, strength, dimensional accuracy, and heat resistance while reducing warping and deformation. With excellent chemical resistance and low moisture absorption, PET CF is ideal for producing lightweight, rigid components that require precision and long-term reliability.
Applications
  • Automobile
  • Aerospace
  • End-use part
  • Jigs & Fixtures
  • Manufacture aids
  • Electrical and electronics (E&E) industry

Documentation

Resistant to Temperature Cycling.

See TDS for Details

Intermediate Material

See TDS for information

Adhesion Aid Recommended

Explore Options

Open Chamber/Active Cooling Recommended

Recommended for best results

Abrasive Material

A hardened nozzle is Required

Technical Specs

Overview
Net Weight 1kg
Material Compatibility
Material Diameter / Thickness 1.75mm

Product Highlights

Top Features

An ideal choice to experience a reliable carbon fiber composite printing for strong and cost-effective end-use applications

Raise3D Industrial PET CF is a carbon fiber-reinforced composite filament based on PET (Polyethylene terephthalate). Well-dispersed 15wt% carbon fibers enhance the rigidity, strength, heat and chemical resistance of the PET matrix. After annealing, PET CF stabilizes its heat resistance at around 150ºC and tensile modulus and strength of over 6 GPa and 80 MPa respectively. Compared to carbon fiber-reinforced Nylon filament, the high printability, dimensional stability, high creep resistance and low moisture absorption makes PET CF an ideal choice for reliable carbon fiber composite printing for strong and cost-effective end-use applications, such as jigs. fixtures, functional parts.

  • HDT up to 150℃
  • Strong and high stiffness
  • High dimensional stability
  • Low moisture absorption
  • Creep and chemical resistance

Printing Guide

Recommended Print Settings

  • Nozzle temperature (°C): 280-300℃
  • Bed temperature (°C): 60-80℃
  • Layer height (mm): 0.1-0.25 mm
  • Printing speed (mm/s): 35-90 mm/s
  • Cooling fan: On
  • Drying temperature (°C): 70-80°C for 8 to 12 hours

Printing Note:

  • Dry PET CF at 70-80°C for 8-12 hours before printing, as low moisture content is crucial for final printed part quality.
  • After drying, we recommend storing PET CF filaments inside Raise3D Filament Dry Box during the printing process.
  • Abrasion of the brass nozzle happens frequently when printing PET CF. Using an abrasion-resistant nozzle, at minimum a Steel nozzle should be used or preferably, a SiC nozzle.
  • After printing, it is recommended to anneal the model in an oven at 80-100°C for 8-12 hours.
  • For a small size model (side length < 50 mm), annealing at 80°C for 8 hours is recommended; For a medium-size model (50 mm < side length < 150 mm), annealing at 80°C for 12 hours is recommended; For a large size model, 100°C for at least 12 hours is recommended.
  • If PET CF is also used as the support material, please remove the support structure after annealing.